Features & Benefits
- Materials Features
- Product Benefits
- Good cosmetic surface and minimal glass print
- Good cycle times and moderate Barcol development
- Easy roll-out and high laminate physical properties
- High resistance to cracking and torsional stress
- Less odor and lower emissions in the shop
- Key Features
- Low Laminate Exotherm
- Moderate Trim Time
- Excellent Fiberglass Wet-Out
- Excellent Toughness
- Less Than 32% HAP (Styrene)
Applications & Uses
- Composites End Use
Properties
- Physical Form
- Typical Properties
Value Units Test Method / Conditions Barcol Hardness (1/4 inch 6 mm laminate) 50 - 934-1 gauge, ASTM D2583 Tensile Elongation (for 1/4 inch 6 mm laminate) 1.24 % ASTM D638 Tensile Modulus (for 1/4 inch 6 mm laminate) 8550 MPa ASTM D638 Tensile Strength (for 1/4 inch 6 mm laminate) 75 MPa ASTM D638 Flexural Modulus (for 1/4 inch 6 mm laminate) 8280 MPa ASTM D790 Flexural Strength (for 1/4 inch 6 mm laminate) 140 MPa ASTM D790 Heat Distortion Temperature (for 1/8 inch 3.2 mm casting) 83 °C ASTM D648 Barcol Hardness (1/8 inch 3.2 mm casting) 35 - 934-1 gauge, ASTM D2583 Tensile Elongation (for 1/8 inch 3.2 mm casting) 1.5 % ASTM D638 Tensile Modulus (for 1/8 inch 3.2 mm casting) 3340 MPa ASTM D638 Tensile Strength (for 1/8 inch 3.2 mm casting) 46 MPa ASTM D638 Flexural Modulus (for 1/8 inch 3.2 mm casting) 3600 MPa ASTM D790 Flexural Strength (for 1/8 inch 3.2 mm casting) 80 MPa ASTM D790 Specific Gravity 1.02 - 1.14 - - Hazardous Air Pollutant (Styrene) max. 32.0 % - Non Volatile Content 66.0 - 70.0 % - Gel to Peak Exotherm Time 127 - 154 °C - Gel Time 7:00-15:00 min:sec - Gel Time (100 grams resin at 77°F 25°C, initiated with 1.00% DDM-9 by volume*) 18:00-23:00 min:sec - Thixotropic Index 2.75-3.40 - - Viscosity (rv #3 spindle at 50 rpm 25°C,) 400 - 525 cPs Brookfield Model RV - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Volatile Organic Compounds (As shipped, including monomers and additives) 29.8 %(w/w) - Relative Density 0.9 - 1.3 - - Vapor Density (Air = 1) 3.6 - - Vapor Pressure (Room Temperature) 0.2 - 0.67 kPa - Explosion Limits (Upper) 6.8 % - Lower Explosion Limit 0.9 % - Evaporation Rate (Butyl Acetate = 1) max. 1 - - Flash Point min. 31 °C Closed cup Boiling Point 145 - 168 °C - Odor Threshold 0.1 ppm - Odor Sweetish - - Appearance Various liquid - -