Features & Benefits
- CASE Ingredients Features
- Product Advantages
- Readily soluble in a wide range of polar and non-polar organic solvents.
- Easily emulsified in water.
Applications & Uses
- Markets
- Applications
- Application Method
- Compatible Substrates & Surfaces
- Coating End Applications
Properties
- Physical Form
- Appearance
- Amber to yellowish liquid
- Soluble in
- Polar organic solvents, Non polar organic solvents
- Typical Properties
Value Units Test Method / Conditions Density 1.06 g/cc - Dynamic Viscosity 1500 - 2400 mPa.s - - SDS Physical and Chemical Properties
Value Units Test Method / Conditions pH Value (at 20°C, 1% suspension in water) 7 - - Density (at 20°C) 1.1 kg/m³ - Vapor Pressure (at 20°C) 1.0*10-⁴ Pa - Ignition Temperature min. 380 °C - Flash Point min. 110 °C - Boiling Point min. 350 °C - Odor None - - Color Yellow - - Physical Form Liquid - - Immiscible in Water (at 20°C) - - - Solubility Data
Value Units Test Method / Conditions 1-Methoxy-2-propylacetate Solubility (at 25°C) min. 50 g/100g solvent - Butyl Acetate Solubility (at 25°C) min. 50 g/100g - Butylcarbitol Solubility (at 25°C) min. 50 g/100g - Methyl Ethyl Ketone Solubility (at 25°C) min. 50 g/100g - Water Solubility (at 25°C) max. 0.1 g/100g - Xylene Solubility (at 25°C) min. 50 g/100g -
Regulatory & Compliance
Technical Details & Test Data
- UV Visible Spectrum Graph
- Experiments
- Resin: Polyurethane (PU) Clear Coating
- Preparations: Air dry for 6 hours
- Exposure Unit: Q-U-V with UVB-313 light ball
- Test Methods: ASTM G154
- Dosage: 2% Solid content
Fig.1-1 Delta Yellowness Index(AYI)
- Application: Spray
- Film Thickness: 90 microns (wet); 25 microns (dry)
- Exposure Time: 1000 hours
- Gloss Retention and Yellowness Index: ASTMG154
Fig.1-2 Gloss Difference
Storage & Handling
- Storage Conditions
Eversorb® 83 should be kept in a dry, dark place without any light exposure.