• Very low CLTE for an improved dimensional stability (smaller gaps) and a better fit and finish for optimal quality
• High ductility and easy flow for more design freedom (larger/longer parts, optimized wall thickness)and better economics (improved cycle time)
• Significant density advantage (up to 10% compared to a PC/PET) for lighter parts and optimized costs
• Faster cycle times for a better process cost control
• High gloss for painted applications with enhanced paint adhesion
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
Properties
- Physical Form
- Mechanical Properties
Value Units Test Method / Conditions Tensile Modulus 4200 MPa ISO 527-1/1 Tensile Strain (at break) 15 % ISO 527-2/5 Tensile Stress (Yield) 52 MPa ISO 527-2/5 - Physical Properties
Value Units Test Method / Conditions Apparent Bulk Density 0.63 g/cc ISO 60 Density 1.25 g/cc ISO 1183 Melt Mass - Flow Rate (at 260°C/5.0 Kg) 24 g/10 min ISO 1133 Molding Shrinkage 0.20 - 0.60 % ISO 294-4 Spiral Flow¹ 52 cm - - Thermal Properties
Value Units Test Method / Conditions CLTE - Flow (-30 to 80°C) 0.000035 - 0.000040 cm/cm/°C ISO 11359-2 Vicat Softening Temperature 122 °C ISO 306/B50 Deflection Temperature Under Load (264 psi, 1.8 Mpa, Unannealed) 105 °C ISO 75-2/A - SDS Physical and Chemical Properties
Value Units Test Method / Conditions Color Black - - Relative Density (water = 1) 1.10 - 1.14 - - Flammability (Solid, Gas) May form combustible dust concentrations in air during processing, handling or other means. - - Odor Odorless - - Physical Form Pallets - - - Impact Properties
Value Units Test Method / Conditions Charpy Notched Impact Strength (at 23°C) 10 kJ/m² ISO 179/1eA - Injection Molding
Value Units Test Method / Conditions Drying Temperature 120 °C - Drying Time 5.5 hrs - Mold Temperature 60 - 80 °C - Processing (Melt Temperature) 255 - 280 °C - - Note
¹Melt Temperature: 500°F (260°C), Injection Pressure: 2.61E+4 psi (1.80E+3 bar)