| Viscosity (at 25°C, #4 Spindle at 20 rpm) | 1,700-2,200 | cPs | Brookfield Model RV |
| Barcol Hardness (1/4 inch 6 mm laminate) | 32 - 36 | - | 934-1 gauge, ASTM D2583 |
| Tensile Elongation (for 1/4 inch 6 mm laminate) | 1.4 | % | ASTM D638 |
| Tensile Modulus (for 1/4 inch 6 mm laminate) | 3810 | MPa | ASTM D638 |
| Tensile Strength (for 1/4 inch 6 mm laminate) | 39 | MPa | ASTM D638 |
| Flexural Modulus (for 1/4 inch 6 mm laminate) | 3590 | MPa | ASTM D790 |
| Flexural Strength (for 1/4 inch 6 mm laminate) | 59 | MPa | ASTM D790 |
| Heat Distortion Temperature (for 1/8 inch 3.2 mm casting) | 104 | °C | ASTM D648 |
| Barcol Hardness (1/8 inch 3.2 mm casting) | 40 | - | 934-1 gauge, ASTM D2583 |
| Tensile Elongation (for 1/8 inch 3.2 mm casting) | 1.8 | % | ASTM D638 |
| Tensile Modulus (for 1/8 inch 3.2 mm casting) | 3800 | MPa | ASTM D638 |
| Tensile Strength (for 1/8 inch 3.2 mm casting) | 70 | MPa | ASTM D638 |
| Flexural Modulus (for 1/8 inch 3.2 mm casting) | 3400 | MPa | ASTM D790 |
| Flexural Strength (for 1/8 inch 3.2 mm casting) | 134 | MPa | ASTM D790 |
| Weight per Gallon | 8.90 - 9.20 | lbs | - |
| Room Temperature Catalyzed Stability (RTCS) | min. 24 | hrs | - |
| Non Volatile Content | 51.0 - 56.0 | % | - |
| Gel to Peak Exotherm Time (at 150°F 66°C to Peak Exotherm, min:sec Peak Exotherm) | 177-232 | °C | - |
| Gel Time | 2:00 - 10:00 | mins | - |
| Gel Time (run in a 140°F 60°C water bath, initiated with 1.0 phr of perkadox 16 and 0.5 phr of trigonox 42s) | 6:00 - 14:00 | mins | - |
| Thixotropic Index | 3.0 - 3.8 | - | - |